HARDOX Wearparts, network, which WINFA, s.r.o. joined in 2004, is a worldwide network of companies that produce spare parts, using their own capabilities and technology, exclusively using HARDOX material, with the possibility to export their production worldwide. Each licensed member of the HARDOX Wearpartsnetwork guarantees to produce spare parts and to provide delivery services of the highest quality.

The current unfavourable situation that has compromised the plans of many companies has only shown the ever-increasing significance of activities aimed at repair or renovation and manufacture of spare parts. Thus making it possible for businesses to save considerable funds that would otherwise have been used for the purchase of new production equipment.

Detailed parameters can be found on the SSAB supplier's website. For more information, click here.

1Hardox Sieve Plates

Abrasion resistant HARDOX sheet metal from 0.7 to 160 mm

Due to the wide variety of dimensions, Hardox is suitable for a broad range of structures and products.

QualityHardness [HBW]Notch toughness at 20-mm thicknessBending t < 8 mm R/tDurabilityCarbon equivalent at 200-mm thicknessThickness [mm]Download (PDF)
Hardox – abrasion-resistant sheet metal that is easy to process, enabling lighter, stronger and more resistant applications.
Hardox HiTuf35095 J/-40°C(3)  0.56/0.38 (3)40-160English
Hardox 40040045 J/-40°C  0.58/0.3740-70(4)English
Hardox 400 Bar40045 J/-40°C2.5(1)10.48/0.293.2-130(5)English
Hardox 45045050 J/-40°C3.0(1)1.1-1.70.56/0.383.2-130English
Hardox 50050037 J/-40°C3.5(1)1.3-2.10.63/0.414-103English
Hardox 55055030 J/-40°C 1.5-4.00.72/0.488-65English
Hardox 60060020 J/-40°C 1.8-8.00.76/0.588-65English
Hardox Extreme650-700<15 J/-40°C 2.0-18.00.65/0.548-19English

All sheet metal is produced with a tolerance in line with Hardox® which is a guarantee of strength.

  • Max./min. lifespan according to SSAB WearCalc (standard steel 0.2-0.8).
  • CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Cu + Ni)/15; CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40
  • 70 mm
  • Bar diameter
  • Thickness up to 160 mm is available upon request.
2Hardox Wear Strips
QualityHardness [HBW]Notch toughnessBending t < 6 mm R/tDurabilityCarbon equivalent at 200-mm thicknessThickness [mm]Download (PDF)
Hardox – abrasion-resistant sheet metal that is cut to a certain length for all purposes, enabling lighter, stronger and more resistant applications.
Hardox 40040045 J/-40°C3.010.48/0.302.0-8.0English
Hardox 45045050 J/-40°C3.01.1-1.70.52/0.352.5-8.0English
Hardox 450450(5)3.50.39/0.310.7-2.1English
Hardox 50050037 J/-40°C3.51.3-2.10.55/0.403.0-6.5English

All sheet metal is produced with a tolerance in line with Hardox® which is a guarantee of strength.

  • Max./min. lifespan according to SSAB WearCalc (standard steel 0.2-0.8).
  • CEV=C+Mn/6+(Cr+Mo+V)/5+(Cu+Ni)/15; CET=C+(Mn+Mo)/10+(Cr+Cu)/20+Ni/40
  • Tested in line with Vickers hardness test
3Hardox Pipe

The exceptional qualities of Hardox abrasion-resistant sheet metal are also available in the form of pipes made of Hardox 500. This provides extended lifespan when dropping high friction material such as wet concrete, soil, gravel or ore.

Hardox 500pipes are rolled and plasma welded with prior to hardening. This guarantees the same mechanical properties of the weld as those of the rest of the material.

AkosťHardness [HBW]Yield gap [MPo]External dimensions, circularWall thickness [mm]Download (PDF)
Hardox 4004001000-130076.1-219.13.00-6.00English
Hardox 500500>120076.1-1332.00-6.00English

Detailed parameters can be found on the supplier’s website SSAB.

1STRENX HOT-ROLLED SHEET STEEL
QualityYield strength [MPa]Toughness at 20-mm thicknessBending properties t < 8 mm R/tYield strength/stress [MPa]Carbon equivalentThickness [mm]Download (PDF)
MinMinMax
Strenx – high-strength steel that allows easier and more innovative assembly.
Strenx 700700(2)165 J/-40°C1.57809300.43/0.294-160(5)English
Strenx 900900(2)88 J/-40°C2.594011000.55/0.364-100(5)English
Strenx 960960(2)84 J/-40°C2.598011500.55/0.364-100English
Strenx 1100110067 J/-40°C3.0125015500.55/0.364-40(5)English
Strenx 1300130032 J/-40°C(3)3.5(4)140017000.65/0.424-10English

All sheet metals are produced with a tolerance in line with Strenx® which is a guarantee of strength.

  • CEV=C+Mn/6+(Cr+Mo+V)/5+(Cu+Ni)/15; CET=C+(Mn+Mo)/10+(Cr+Cu)/10+Ni/40 10 mm (8 mm above MPa)
  • Thickness of 4-53 mm
  • For a thickness of 6 mm, 1/2 testing sample shall be used
  • t < 6: 3.5 ŧ > 6: 40
  • Thicker materials are available upon request; Strenx 700:170 mm, Strenx 900:120 mm, Strenx 1100:50 mm up to 160 mm are available upon request.
2STRENX HOT-ROLLED AND COLD-ROLLED STEEL
QualityYield strength [MPa]Yield strength/stress [MPa]Ductility A(5)[%]Bending radius of 90°when bending 6 mmCarbon equivalent at 6-mm thicknessThickness [mm]Download (PDF)
MinMinMaxMinMin
Strenx 100 XF100(1)110(1)15(2)1.21/2″-3/8 (3)English
Strenx 100 XF110118(1)15(2)1.21/2″-3/8″ (3)English
Strenx MC – vhigh-strength steel manufactured for cold forming of stronger and lighter structures.
Strenx 600 MC600650820161.10.33/0.212.0-10.0English
Strenx 650 MC650700850141.20.34/0.222.0-10.0English
Strenx 700 MC700750950121.20.39/0.252.0-10.0English
Strenx 700 MC+700750950131.00.38/0.243.0-12.0English
Strenx 900 MC900930120083.00.50/0.513.0-10.0English
Strenx 900 +9009301200113.00.50/0.343.0-6.0English
Strenx 960 MC960980125073.50.51/0.283.0-10.0English
Strenx 960 +9609801250103.50.50/0.343.0-6.0English
Strenx 1100 MC11001200146064.00.50/0.343.0-8.0English
Cold-rolled Strenx steel – high-strength structural steel for the manufacture of stronger and lighter structures.
Strenx 700 CR70010012007(4)2.00.40/0.290.70-2.10English
Strenx 960 CR960120014003(4)3.50.39/0.280.70-2.10English
Strenx 1100 CR1100130015003(4)3.50.41/0.300.70-2.10English
  • Ksi
  • Ductility A(50)Min.
  • Inches
  • Inches A(80)Min.
  • CEV=C+Mn/6+(Cr+Mo+V)/5+(Cu+Ni)/15; CET=C+(Mn+Mo)/10+(Cr+Cu)/20+Ni/40
3STRENX HOLLOW SECTIONS
QualityYield strength [MPa]Notch toughnessYield strength/stress [MPa]Carbon equivalentWall thickness [mm]Download (PDF)
MinMinMax
Strenx hollow sections – improved high-strength cold-moulded hollow sections.
Strenx Section 65065027J/-40°7009500.24/0.222.50-10.0English
Strenx Section 70070027J/-40°7509500.38/0.242.50-10.0English
Strenx Section 90090027J/-40°93012000.51/0.283.6-6.0English
  • CEV=C+Mn/6+(Cr+Mo+V)/5+(Cu+Ni)/15; CET=C+(Mn+Mo)/10+(Cr+Cu)/20+Ni/40
4STRENX STEEL SECTIONS
QualityYield strength [MPa]Notch toughnessYield strength/stress [MPa]Carbon equivalentWall thickness [mm]Download (PDF)
MinMinMax
Strenx sections –improved high-strength hollow sections
Strenx Tube 700QLH70040J/-40°7809300.48/0.342.3-6.3English
Strenx Tube 700MLH70027J/-50°7509500.38/0.243.0-10.0English
Strenx Tube 700MH70040J/-20°7509500.38/0.243.0-8.0English
Strenx Tube 900MH90040J/-20°93012000.50/0.254.0-6.0English
Strenx Tube 960MH96040J/-20°98012500.51/0.284.0-6.0English
  • CEV=C+Mn/6+(Cr+Mo+V)/5+(Cu+Ni)/15; CET=C+(Mn+Mo)/10+(Cr+Cu)/20+Ni/40

Detailed parameters can be found on the supplier’s website: SAAB.

1TOOLOX SHEET METAL
ProductThickness
(mm)
Hardness 1)
(HBW)
Testing temperature Impact energy, Charpy-V, Min JDownload (PDF)
TOOLOX 335 – 130275 – 32520°C35 min J 2)English
TOOLOX 406 – 130360 – 42020°C20 min J 2)English
TOOLOX 446 – 130410 – 47520°C18 min J 3)English
  • Hardness is measured as per EN ISO 6506-1 on a milled surface of 0.5 – 2 mm below the sheet surface.
  • Impact test as per EN 10 025, EN ISO 148 with a 2-mm striker
  • Impact test as per EN 10 025, EN ISO 148

Ultrasound testing

Ultrasound testing shall be carried out as per EN 10 160 with extra requirements in line with SSAB V6 specification

TOLERANCES

More details can be found in SSAB’s brochure 41-General product information Strenx, Hardox, Armox and Toolox-UK or on www.toolox.com

2TOOLOX MECHANICAL PROPERTIES
ProductThickness
(mm)
Hardness 1)
(HBW)
Testing temperature Impact energy, Charpy-V, Min JDownload (PDF)
TOOLOX 3321 – 141275 – 32520°C35 min J 2)English
TOOLOX 4421 – 141410 – 47520°C18 min J 3)English
  • Hardness of bar is measured as per EN ISO 6506-1 on a milled surface of 0.5 – 2 mm below the sheet surface. Hardness of bars is measured on a milled surface, with cuts distributed as per impact testing to EN 10 083.
  • Impact test as per EN 10 083.
  • Impact test as per EN 10 025, EN ISO 148.

Ultrasound testing

Ultrasound testing shall be carried out as per EN 10 308 with additional requirements in line with SSAB V6 specification

TOLERANCES

More details can be found in SSAB’s brochure 41-General product information Strenx, Hardox, Armox and Toolox-UK or on www.toolox.com

Diameter and length

Tolerances as per EN 10 060.

Flatness

Tolerances as per EN 10 060.

Surface propertie

Peeled surface

Machining

Thanks to its low carbon content, Toolox has an excellent machinability.

Toughness

Low carbon content and very high cooling rates are the main reasons why Toolox is 2-3 times tougher than comparable steels of similar hardness. The high hardness, in combination with excellent toughness ensures lower tool wear and high output levels when the tool is in service.

Fatigue

Thanks to the high cleanliness of alloying elements, the surface is highly glossy after machining, which also increases its fatigue-resistance. In of applications where greater hardness is required due to wear resistance, Toolox may be nitrided, applied through PVD coating. Toolox may also be used with applications where working temperatures up to 592°C are required.

Detailed parameters can be found on the supplier’s website: SSAB.

1Docol ocele a hrúbka
Steel typeThickness
(mm)
Download (PDF)
Docol 420 LA0,50 – 2,10English
Docol 500 LA0,50 – 2,10English
Docol 800 Roll0,50 – 2,10
Docol 1000 Roll0,50 – 2,10
Docol 500 DP0,50 – 2,10English
Docol 500 DL0,50 – 2,10
Docol 600 DP0,50 – 2,10English
Docol 600 DL0,50 – 2,10
Docol 600 GC0,50 – 2,10
Docol 800 DP0,50 – 2,10English
Docol 800 DL0,50 – 2,10
Docol 1000 DP0,50 – 2,10English
Docol 1000 DPZE0,50 – 2,10
Docol 900 M0,50 – 2,10English
Docol 900 MZE0,50 – 2,10
Docol 1200 M0,50 – 2,10English
Docol 1200 MZE0,50 – 2,10
Docol 1400 M0,50 – 2,10English
Docol 1400 MZE0,50 – 2,10
Docol 1500 M0,50 – 2,10English
Docol 700 W0,50 – 2,10
Docol Strap 800
Docol Strap 930
Dogal 420 LAD0,50 – 2,50
Dogal 460 LAD0,80 – 2,50
Dogal 500 LAD0,80 – 2,50
Dogal 800 Roll0,80 – 2,00
Dogal 1000 Roll0,80 – 2,00
Dogal 500 DP0,70 – 2,00
Dogal 600 DP0,80 – 2,00
Dogal 800 DP0,80 – 2,00
Dogal 800 DPX0,80 – 2,00
Dogal 1000 DPX0,80 – 2,00

Detailed parameters can be found on the supplier’s website: SSAB.

1Armox protection plate
Steel typeThickness
(mm)
Download (PDF)
Armox 300T3.0-5.0
Armox 340T5.0-50.0
Armox 370T 13.0-100.0English
Armox 370T 23.0-100.0English
Armox 440T4.0-30.0English
Armox 500T3.0-80.0English
Armox 560T5.0-100.0
Armox 600T4.0-20.0English
Armox Advance4.0-7.9English

Detailed parameters can be found on the supplier’s website: SSAB.

1Duroxite
ProductDescriptionOverlay propertiesApplications
DuroxiteTM 100DuroxiteTM 100 is fabricated by depositing chromium-rich abrasion- resistant materials on mild steel backing. The hardfacing overlay is suitable for severe abrasive wear and moderate to low impact applications. It offers in both plate and pipe.Bulk hardness: Single pass 55 to 57 HRC Double passes 56 to 59 HRC Triple and more passes 58 to 63 Carbide hardness: 1700 HK. Volume fraction of carbides: 30-50% ASTM G65-Procedure. A weight loss: 0.19g max.Liners for truck bed, dozer blade, bucket and excavator, chute /hopper, discharge cone, dredging pipe, dredging pump, blast furnace liner, fan blade, coke vibrating screen plate, coal handling chute, coal feeder liner, crusher screen plate, classifier cone, journal liner, silo bunkers.
DuroxiteTM 101DuroxiteTM 101 is to weld chormium-riched carbide overlay on quench & tempered (Q&T) steel backing plate. The overlay has same wear properties as DuroxiteTM 100, but with a better impact resistance and greater safety margin compared to mild steel backing due to employing stronger Q&T base metal.Bulk hardness: Single pass 55 to 57 HRC. Double passes 56 to 59 HRC. Triple passes 58 to 63 Carbide hardness: 1700 HK. Volume fraction of carbides: 30-50% ASTM G65-Procedure A weight loss: 0.19g max.Coal discharger chute, loader bucket liner, bucket lip shroud, bucket side shroud
DuroxiteTM 200DuroxiteTM 200 is composed of primary chromium-rich carbides with extremely hard secondary carbides dispersed in an austenite matrix. The hardfacing components are suitable to apply in extremely severe abrasion wear and heavy impact up to 572°F (300 °C). The overlay provides 2 to 3 times longer service life than DuroxiteTM 100. It offers in both plate and pipe.Bulk hardness: 60 to 65 HRC Carbide hardness: 2000 HK. Volume fraction of carbides: 30-50% ASTM G65-Procedure A weight loss: 0.12g max.Buckets and teeth, sizing screens, railway ballast tampers, coke hammers, dredge buckets and lips, dragline buckets, rippers, crushing equipment, brick industry components, Muller tyres, catalyst lift pipes, pump impellers, fan blades, rockwool rolls, wear plates operating at high temperature in the steelmaking industry.
DuroxiteTM 210DuroxiteTM 210 applies specially formulated abrasive materials depositing on mild steel backing plate subject to extremely severe abrasive wear and moderate impact up to 1112°F (600°C). The longer service life would be offerred compared to DuroxiteTM 200. It offers in both plate and pipe.Bulk hardness: 60 to 65 HRC Carbide hardness: 2500-3000 HK. Volume fraction of carbides: 30-50% ASTM G65-Procedure A weight loss: 0.12g max.Cement furnace components, sinter plant parts, fan blades, mixer blades, crews, Gyratory mantles, coal & cement pulverizer rolls & grinding, Ore sintering, crushing, riddling, blast furnace hoppers and throats, ovens
DuroxiteTM 201DuroxiteTM 201 overlay is composed of a high concentraion primary chromium carbides and secondary carbides deposition on Q&T steel backing. Besides the same wear properties as DuroxiteTM 200, DuroxiteTM 201 also provides better impact resistance and greater safety margin than DuroxiteTM 200.Bulk hardness: 60 to 65 HRC Carbide hardness: 2000 HK. Volume fraction of carbides: 30-50% ASTM G65-Procedure. A weight loss: 0.12g max.Loader bucket liner, feeding system for ball mill.
DuroxiteTM 211DuroxiteTM 211 overlay contains primary chromium carbides and refined multiple- alloys complex carbides in an austenite matrix which is deposited on Q&T steel backing. Besides the same wear properties as DuroxiteTM 210, DuroxiteTM 211 also provides better impact resistance and greater safety margin than DuroxiteTM 210.Bulk hardness: 60 to 65 HRC Carbide hardness: 2500-3000 HK. Volume fraction of carbides: 30-50% ASTM G65-Procedure A weight loss: 0.12g max.screen plate
DuroxiteTM 400DuroxiteTM 400 is manufactured by depositing special formulated abrasive alloys on Q&T steel bar to apply for metal- to-metal wear application up to 900°F (482°C). The overlay is composed of martensite with a network of carbides.Hardness: 52 to 54 HRC. Work hardening hardness: 58 HRCDragline shovel, clam shell buckets, sheave pins, backhoe pins, crusher shafts